Zro2 Zirconium Oxide Zirconia Ceramic Cutting Knife Sharp Blade

Product Description

Zirconia ceramics

Advantages:
1. High strength and high hardness;
2. Good abrasion resistance;
3. High toughness;
4. Low friction coefficient;
5. Good corrosion resistance;
6. Low thermal conductivity;
7. The modulus of elasticity and coefficient of thermal expansion are close to metals.


Details:
1.Zirconia ceramics have the advantages of high hardness, good wear resistance, high toughness, low

coefficient of friction, and good corrosion resistance. They are widely used in mechanical seals, ball milling media, cutting tools, ceramic bearings,automotive engine parts, etc.
2.The wear resistance of zirconia ceramics is 15 times that of alumina ceramics. The friction coefficient of

zirconia ceramics is only 1/2 of that of alumina ceramics, while the friction coefficient of alumina ceramics is

very low.

3.The density of zirconia ceramics is higher than that of alumina ceramics. The density of alumina ceramics is 3.5. The density of zirconia ceramics is 6. The texture is more delicate. After grinding, the surface finish is higher than

9. It is mirror-like,extremely smooth, and has a smaller coefficient of friction.

4.In addition, the toughness of zirconia ceramics is excellent, which overcomes the inherent brittleness of the

ceramics, has higher wear resistance, and greatly extends the service life of the product.

Applications of zirconia ceramic

* Structural ceramics:
Mainly include: Y-TZP grinding ball, nozzle, ball valve ball seat, fiber optic sleeve, drawing die and cutting tool,
wear-resistant cutter, case and strap, bracelet and pendant, ball bearing, etc.

* Functional ceramics:
Used as induction heating tubes, refractory materials, and heating elements. Used in fields such as oxygen sensors, solid oxide
fuel cells, and high-temperature heating elements.

In addition, zirconia is widely used in thermal barrier coatings, catalyst carriers, medical, health care, refractory materials,
textiles and other fields.
 

Chemical component:95%ZrO2,5%Y2O3
Density	g/cm3	6.02
Water absorption	%	0
Sintering temperature	C	1540
Hardness	HV	1360
Flexural strength	Mpa	1400
Compressive strength	Mpa	2500
Fracture toughness	Mpa.m3/2	7
Thermal expansion coefficient	/C	10.2*10-6
Thermal shock resistance	T(C)	360
Thermal conductivity	W/m.k(25-300C)	2