High Temperature Inorganic Glue for Ceramic and Aluminosilicate
Product Details
| Customization: | Available |
|---|---|
| Usage: | Ceramic Glue |
| Temperature: | 1400c, 1700, 900c |
Shipping
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
Payment Guarantee
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Secured Trading Service
Diamond Member Since 2021
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
Importers and Exporters
High Repeat Buyers Choice
The supplier has import and export rights
More than 50% of buyers repeatedly choose the supplier
Sign In to see all verified strength labels (16)
Find Similar Products
Basic Info.
- Model NO.
- YN-049
- Type
- C-2, C-3, Cps
- Transport Package
- Plywood Case
- Specification
- CUSTOMIZED
- Trademark
- Yunnuo
- Origin
- China
- HS Code
- 8547100000
Packaging & Delivery
- Package Size
- 10.00cm * 10.00cm * 3.00cm
- Package Gross Weight
- 1.000kg
Product Description
|
Property of condensate
|
C-2
|
C-3
|
CPS cupric oxide
|
|
Color
|
gray
|
gray
|
black
|
|
Heat resistant temperature C
|
1730
|
1460
|
980
|
|
Hardness
|
Hard,brittle
|
Hard,brittle
|
Hard,brittle
|
|
Electrical properties
|
Good insulation performance at high temperature
|
Good insulation performance at high temperature
|
Good insulation at room temperature
|
|
Medium resistance
|
Oil resistant, acid and alkali resistant, not resistant to boiling water
|
Oil resistant, acid and alkali resistant, not resistant to boiling water
|
Oil resistant, acid and alkali resistant, not resistant to boiling water
|
|
Coefficient of linear expansion
|
Similar to ceramic(80×10-6/C)
|
Similar to steel(12.9×10-6/C)
|
Close to steel,
Slightly contracted |
|
Socket strength / tensile strength (steel-steel)Mpa
|
82/37
|
79/34
|
96/-
|
|
Applied range
|
High-temperature instrumentation, electronics, temperature-measuring element coating and potting, high-temperature anti-oxidation
coating of metal materials, ceramics and other high-temperature bonding |
Bonding and potting of high temperature resistant metal parts, high temperature oxidation resistant coating of metal materials,
high temperature resistant bonding of metal materials |
Metal sleeve sticking,
the bonding of tool measuring tools |
|
Proportion of glue solid phase
|
1.6-2.5g
|
1.6-2.5g
|
3.5-5.5g
|
|
Proportion of glue liquid phase
|
1ml(about 1.39g)
|
1ml(about 1.39g)
|
1ml (about 1.7g)
|
|
Curing procedures
|
Room temperature 12-24 hours → 80C 2 hours → 150C 2 hours, cool slowly
|
Room temperature 12-24 hours → 80C 2 hours → 150C 2 hours, cool slowly
|
Slow heating,→ 80C 2 hours → 150C 2 hours, cool slowly
|
|
Net weight
|
500g
|
500g
|
750g
|
HT-CPS high temperature structural adhesive
Physical state: powder + liquid
Operating time: 30min
Curing conditions: 1. room temperature 12h; 2.80 C 2h; 3.150 C 2h
Colour: Black
Density (g/cm3): 3.5
Shear strength (MPa) GB / T7124-1999: 86 (socket)
Impact strength (J / cm2) GB / T6328-1986: 8
Tensile strength (MPa) GB / T6329-1996: 38.5
Peel strength (N / cm) GB / T2791-1981: ---
Working temperature (C): -196 ~ 980
Heat-resistant temperature: 980 ºC
Weight: 750g per group
Material: Inorganic copper oxide, temperature resistance 980 ºC.
Uses: Used for bonding various hard alloy and ceramic turning tools, milling cutters, drills or gear cutters. The socket strength
is extremely high, which can be used to make extension rods and repair defects in high temperature casting conditions.
Use operation
1. Roughen the bonding surface and remove rust, oil and grease. The joint design is best with socket.
2. Glue adjustment: The solid and liquid phases of various types of glue are adjusted according to the ratio of the technical index table, and it should be adjusted to a uniform and flowable paste. CPS copper oxide inorganic glue should not be excessively adjusted each time. It is best to adjust the glue on the containers (such as copper) that dissipate quickly.
3. Curing with glue
Apply (fill) the glue to the surface to be bonded (sealed), and apply a little contact pressure to cure it after assembly. If the
strength is not high and medium resistance is not required, it can be cured at room temperature. Otherwise, please follow the curing procedure of the technical specification table.
Physical state: powder + liquid
Operating time: 30min
Curing conditions: 1. room temperature 12h; 2.80 C 2h; 3.150 C 2h
Colour: Black
Density (g/cm3): 3.5
Shear strength (MPa) GB / T7124-1999: 86 (socket)
Impact strength (J / cm2) GB / T6328-1986: 8
Tensile strength (MPa) GB / T6329-1996: 38.5
Peel strength (N / cm) GB / T2791-1981: ---
Working temperature (C): -196 ~ 980
Heat-resistant temperature: 980 ºC
Weight: 750g per group
Material: Inorganic copper oxide, temperature resistance 980 ºC.
Uses: Used for bonding various hard alloy and ceramic turning tools, milling cutters, drills or gear cutters. The socket strength
is extremely high, which can be used to make extension rods and repair defects in high temperature casting conditions.
Use operation
1. Roughen the bonding surface and remove rust, oil and grease. The joint design is best with socket.
2. Glue adjustment: The solid and liquid phases of various types of glue are adjusted according to the ratio of the technical index table, and it should be adjusted to a uniform and flowable paste. CPS copper oxide inorganic glue should not be excessively adjusted each time. It is best to adjust the glue on the containers (such as copper) that dissipate quickly.
3. Curing with glue
Apply (fill) the glue to the surface to be bonded (sealed), and apply a little contact pressure to cure it after assembly. If the
strength is not high and medium resistance is not required, it can be cured at room temperature. Otherwise, please follow the curing procedure of the technical specification table.
Product name: HT C-2 ultra high temperature repair agent
Physical state: solid+liquid
Operating time: 30min
Curing conditions: 1.) Room temperature 12h; 2.) 80C -150C 2h; 3.) Slow cooling
Color: off-white
Density (g /cm3): 1.4
Compressive strength (MPa) GB / T1041-1992: 82 (socket strength)
Shear strength (MPa) GB / T7124-1999: 37 (tensile strength)
Bending strength (MPa) GB / T1024-1992:-
Insulation strength (kv / mm) GB / T2411-1980: 30
Working temperature (C): -60 ~ 1730
Net weight: 500g two-component
Uses: Inorganic ceramic material, temperature resistance 1730 C. It can repair equipment working under high temperature
conditions, such as repairing damaged or broken acid resistant tanks, blast furnace lining, steel ingot molds and other equipment,burner ignition devices, potting of molten steel temperature probes, etc.
Physical state: solid+liquid
Operating time: 30min
Curing conditions: 1.) Room temperature 12h; 2.) 80C -150C 2h; 3.) Slow cooling
Color: off-white
Density (g /cm3): 1.4
Compressive strength (MPa) GB / T1041-1992: 82 (socket strength)
Shear strength (MPa) GB / T7124-1999: 37 (tensile strength)
Bending strength (MPa) GB / T1024-1992:-
Insulation strength (kv / mm) GB / T2411-1980: 30
Working temperature (C): -60 ~ 1730
Net weight: 500g two-component
Uses: Inorganic ceramic material, temperature resistance 1730 C. It can repair equipment working under high temperature
conditions, such as repairing damaged or broken acid resistant tanks, blast furnace lining, steel ingot molds and other equipment,burner ignition devices, potting of molten steel temperature probes, etc.
){kind=link}
Send your message to this supplier
People who viewed this also viewed
Product Groups
More
Find Similar Products By Category
- Supplier Homepage
- Products
- Special items
- High Temp Adhesive
- High Temperature Inorganic Glue for Ceramic and Aluminosilicate
Related Categories
Hot Searches
More